Razvoj nosača lekovitih supstanci tipa polielektrolitnih kompleksa hitozan/ksantan: karakterizacija procesa rehidratacije in vitro
Development of drug delivery systems based on chitosan/xanthan polyelectrolyte complexes: in vitro characterization of rehydration process
Апстракт
Polielektrolitni kompleksi (PEC) nastaju uspostavljanjem jonskih interakcija između polimera
pri pH oko njihovih pKa. Formiranje i kapacitet PEC za rehidrataciju u fiziološkim tečnostima,
koje može uticati na mehanizam i brzinu oslobađanja aktivne supstance, može zavisiti od
pH i prirode medijuma. Cilj rada je ispitivanje uticaja pH medijuma i upotrebljene kiseline na
rehidrataciju čvrstih PEC hitozana i ksantana. Pripremljeni hidrogelovi tipa PEC ksantana i
hitozana pri pH 3,6; 4,6 i 5,6, upotrebom hlorovodonične (HK) i sirćetne (SK) kiseline su osušeni,
usitnjeni i upotrebljeni za izradu vodenih disperzija u koncentracijama 2% i 4% na šejkeru LSB18
(Grant, Velika Britanija) tokom 24 h, na 37±1 °C i 100 o/min. Primenjena je metoda kontrolisane
brzine smicanja koja raste od 0 do 100 s-1, a zatim opada do 0 s-1 tokom 400 s na 37±0,1 °C na
reometru Rheolab MC120 (Paar Physica, Nemačka) sa mernim uređajem Z3 DIN. Posle 24 h
uzorci su bili potpuno hidratisani. Reogrami svih dispe...rzija pokazuju proticanje sa tiksotropijom.
Najveće vrednosti tiksotropije određene su kod PEC pripremljenih pri pH 3,6, a najmanje pri
pH 4,6, nezavisno od korišćene kiseline i koncentracije PEC u disperziji. Struktuiranost uzoraka
procenjena je na osnovu vrednosti prividnog viskoziteta (ηmin na 100 s-1/ ηmax na 22,2 s-1).
Najveće vrednosti η pri koncentraciji 4% imali su uzorci pripremljeni sa SK pri pH 5,6 (1440/5450
mPa·s), a najmanje sa HK pri pH 4,6 (979/3440 mPa·s). Pri koncentraciji 2% najveće vrednosti
η imali su uzorci pripremljeni sa HK pri pH 3,6 (557/2010 mPa·s), a najmanje sa HK pri pH 4,6
(198/692 mPa·s). Može se zaključiti da su izbor kiseline i pH medijuma značajno uticali na jačinu
interakcija između polimera, i posledično na strukturu čvrstih PEC i reološke karakteristike
nakon hidratacije, što se može odraziti na kinetiku oslobađanja aktivnih supstanci.
Polyelectrolyte complexes (PECs) are formed by establishing ion interactions between
polymers at pH around their pKa. Formation and PEC rehydration capacity in physiological
fluids, which can affect the active substance release mechanism and rate, might depend on pH
and medium composition. The aim of this study is to examine the influence of pH of medium
and acid choice on rehydration of solid chitosan/xanthan PECs. Prepared chitosan/xanthan PEC
hydrogels at pH 3.6, 4.6 and 5.6 using hydrochloric (HA) and acetic (AA) acid were dried and
used for aqueous dispersions preparation at concentrations of 2% and 4% on LSB18 shaker
(Grant, UK) during 24 h, at 37±1 °C and 100 rpm. Controlled shear rate measurements were
performed on rheometer Rheolab MC120 (Paar Physica, Germany) with Z3 DIN measuring
device by increasing shear rate from 0 to 100 s-1 and back to 0 s-1, during 400 s at 37±0.1 °C.
Samples were completely hydrated after 24 h. All dispersions rheograms demonstrated flow
w...ith thixotropy. The highest thixotropy values were determined for PECs prepared at pH 3.6,
and lowest at pH 4.6, independently of the used acid and PEC concentration. Sample structure
estimation was based on apparent viscosities (ηmin at 100 s-1/ηmax at 22.2 s-1). The highest η
at concentration of 4% had samples prepared with AA at pH 5.6 (1440/5450 mPa·s), and lowest
with HA at pH 4.6 (979/3440 mPa·s). At concentration of 2%, highest η had samples prepared
with HA at pH 3.6 (557/2010 mPa·s), and lowest with HA at pH 4.6 (198/692 mPa·s). It can be
concluded that acid choice and pH of medium significantly influenced the interaction intensity
between polymers, and consequently, solid PECs structure and rheological characteristics
after hydration, which can be reflected in active substance release kinetics.
Кључне речи:
polielektrolitni kompleks / rehidratacija / prividni viskozitet / polyelectrolyte complex / rehydration / apparent viscosityИзвор:
Treći kongres farmaceuta Crne Gore sa međunarodnim učešćem, 2019. Budva, Bečići, Crna Gora, Zbornik sažetaka, 2019, 224-225Издавач:
- Farmaceutska komora Crne Gore
- Univerzitet Crne Gore, Medicinski fakultet, studijski program-farmacija
Финансирање / пројекти:
- Развој производа и технологија које обезбеђују жељено ослобађање лековитих супстанци из чврстих фармацеутских облика (RS-MESTD-Technological Development (TD or TR)-34007)
Напомена:
- Treći kongres farmaceuta Crne Gore sa međunarodnim učešćem "Novi horizonti u farmaciji - izazovi i mogućnosti", 09.-12. maj 2019. godine, Budva, Bečići
Институција/група
PharmacyTY - CONF AU - Ćirić, Ana AU - Đekić, Ljiljana PY - 2019 UR - https://farfar.pharmacy.bg.ac.rs/handle/123456789/5368 AB - Polielektrolitni kompleksi (PEC) nastaju uspostavljanjem jonskih interakcija između polimera pri pH oko njihovih pKa. Formiranje i kapacitet PEC za rehidrataciju u fiziološkim tečnostima, koje može uticati na mehanizam i brzinu oslobađanja aktivne supstance, može zavisiti od pH i prirode medijuma. Cilj rada je ispitivanje uticaja pH medijuma i upotrebljene kiseline na rehidrataciju čvrstih PEC hitozana i ksantana. Pripremljeni hidrogelovi tipa PEC ksantana i hitozana pri pH 3,6; 4,6 i 5,6, upotrebom hlorovodonične (HK) i sirćetne (SK) kiseline su osušeni, usitnjeni i upotrebljeni za izradu vodenih disperzija u koncentracijama 2% i 4% na šejkeru LSB18 (Grant, Velika Britanija) tokom 24 h, na 37±1 °C i 100 o/min. Primenjena je metoda kontrolisane brzine smicanja koja raste od 0 do 100 s-1, a zatim opada do 0 s-1 tokom 400 s na 37±0,1 °C na reometru Rheolab MC120 (Paar Physica, Nemačka) sa mernim uređajem Z3 DIN. Posle 24 h uzorci su bili potpuno hidratisani. Reogrami svih disperzija pokazuju proticanje sa tiksotropijom. Najveće vrednosti tiksotropije određene su kod PEC pripremljenih pri pH 3,6, a najmanje pri pH 4,6, nezavisno od korišćene kiseline i koncentracije PEC u disperziji. Struktuiranost uzoraka procenjena je na osnovu vrednosti prividnog viskoziteta (ηmin na 100 s-1/ ηmax na 22,2 s-1). Najveće vrednosti η pri koncentraciji 4% imali su uzorci pripremljeni sa SK pri pH 5,6 (1440/5450 mPa·s), a najmanje sa HK pri pH 4,6 (979/3440 mPa·s). Pri koncentraciji 2% najveće vrednosti η imali su uzorci pripremljeni sa HK pri pH 3,6 (557/2010 mPa·s), a najmanje sa HK pri pH 4,6 (198/692 mPa·s). Može se zaključiti da su izbor kiseline i pH medijuma značajno uticali na jačinu interakcija između polimera, i posledično na strukturu čvrstih PEC i reološke karakteristike nakon hidratacije, što se može odraziti na kinetiku oslobađanja aktivnih supstanci. AB - Polyelectrolyte complexes (PECs) are formed by establishing ion interactions between polymers at pH around their pKa. Formation and PEC rehydration capacity in physiological fluids, which can affect the active substance release mechanism and rate, might depend on pH and medium composition. The aim of this study is to examine the influence of pH of medium and acid choice on rehydration of solid chitosan/xanthan PECs. Prepared chitosan/xanthan PEC hydrogels at pH 3.6, 4.6 and 5.6 using hydrochloric (HA) and acetic (AA) acid were dried and used for aqueous dispersions preparation at concentrations of 2% and 4% on LSB18 shaker (Grant, UK) during 24 h, at 37±1 °C and 100 rpm. Controlled shear rate measurements were performed on rheometer Rheolab MC120 (Paar Physica, Germany) with Z3 DIN measuring device by increasing shear rate from 0 to 100 s-1 and back to 0 s-1, during 400 s at 37±0.1 °C. Samples were completely hydrated after 24 h. All dispersions rheograms demonstrated flow with thixotropy. The highest thixotropy values were determined for PECs prepared at pH 3.6, and lowest at pH 4.6, independently of the used acid and PEC concentration. Sample structure estimation was based on apparent viscosities (ηmin at 100 s-1/ηmax at 22.2 s-1). The highest η at concentration of 4% had samples prepared with AA at pH 5.6 (1440/5450 mPa·s), and lowest with HA at pH 4.6 (979/3440 mPa·s). At concentration of 2%, highest η had samples prepared with HA at pH 3.6 (557/2010 mPa·s), and lowest with HA at pH 4.6 (198/692 mPa·s). It can be concluded that acid choice and pH of medium significantly influenced the interaction intensity between polymers, and consequently, solid PECs structure and rheological characteristics after hydration, which can be reflected in active substance release kinetics. PB - Farmaceutska komora Crne Gore PB - Univerzitet Crne Gore, Medicinski fakultet, studijski program-farmacija C3 - Treći kongres farmaceuta Crne Gore sa međunarodnim učešćem, 2019. Budva, Bečići, Crna Gora, Zbornik sažetaka T1 - Razvoj nosača lekovitih supstanci tipa polielektrolitnih kompleksa hitozan/ksantan: karakterizacija procesa rehidratacije in vitro T1 - Development of drug delivery systems based on chitosan/xanthan polyelectrolyte complexes: in vitro characterization of rehydration process SP - 224 EP - 225 UR - https://hdl.handle.net/21.15107/rcub_farfar_5368 ER -
@conference{ author = "Ćirić, Ana and Đekić, Ljiljana", year = "2019", abstract = "Polielektrolitni kompleksi (PEC) nastaju uspostavljanjem jonskih interakcija između polimera pri pH oko njihovih pKa. Formiranje i kapacitet PEC za rehidrataciju u fiziološkim tečnostima, koje može uticati na mehanizam i brzinu oslobađanja aktivne supstance, može zavisiti od pH i prirode medijuma. Cilj rada je ispitivanje uticaja pH medijuma i upotrebljene kiseline na rehidrataciju čvrstih PEC hitozana i ksantana. Pripremljeni hidrogelovi tipa PEC ksantana i hitozana pri pH 3,6; 4,6 i 5,6, upotrebom hlorovodonične (HK) i sirćetne (SK) kiseline su osušeni, usitnjeni i upotrebljeni za izradu vodenih disperzija u koncentracijama 2% i 4% na šejkeru LSB18 (Grant, Velika Britanija) tokom 24 h, na 37±1 °C i 100 o/min. Primenjena je metoda kontrolisane brzine smicanja koja raste od 0 do 100 s-1, a zatim opada do 0 s-1 tokom 400 s na 37±0,1 °C na reometru Rheolab MC120 (Paar Physica, Nemačka) sa mernim uređajem Z3 DIN. Posle 24 h uzorci su bili potpuno hidratisani. Reogrami svih disperzija pokazuju proticanje sa tiksotropijom. Najveće vrednosti tiksotropije određene su kod PEC pripremljenih pri pH 3,6, a najmanje pri pH 4,6, nezavisno od korišćene kiseline i koncentracije PEC u disperziji. Struktuiranost uzoraka procenjena je na osnovu vrednosti prividnog viskoziteta (ηmin na 100 s-1/ ηmax na 22,2 s-1). Najveće vrednosti η pri koncentraciji 4% imali su uzorci pripremljeni sa SK pri pH 5,6 (1440/5450 mPa·s), a najmanje sa HK pri pH 4,6 (979/3440 mPa·s). Pri koncentraciji 2% najveće vrednosti η imali su uzorci pripremljeni sa HK pri pH 3,6 (557/2010 mPa·s), a najmanje sa HK pri pH 4,6 (198/692 mPa·s). Može se zaključiti da su izbor kiseline i pH medijuma značajno uticali na jačinu interakcija između polimera, i posledično na strukturu čvrstih PEC i reološke karakteristike nakon hidratacije, što se može odraziti na kinetiku oslobađanja aktivnih supstanci., Polyelectrolyte complexes (PECs) are formed by establishing ion interactions between polymers at pH around their pKa. Formation and PEC rehydration capacity in physiological fluids, which can affect the active substance release mechanism and rate, might depend on pH and medium composition. The aim of this study is to examine the influence of pH of medium and acid choice on rehydration of solid chitosan/xanthan PECs. Prepared chitosan/xanthan PEC hydrogels at pH 3.6, 4.6 and 5.6 using hydrochloric (HA) and acetic (AA) acid were dried and used for aqueous dispersions preparation at concentrations of 2% and 4% on LSB18 shaker (Grant, UK) during 24 h, at 37±1 °C and 100 rpm. Controlled shear rate measurements were performed on rheometer Rheolab MC120 (Paar Physica, Germany) with Z3 DIN measuring device by increasing shear rate from 0 to 100 s-1 and back to 0 s-1, during 400 s at 37±0.1 °C. Samples were completely hydrated after 24 h. All dispersions rheograms demonstrated flow with thixotropy. The highest thixotropy values were determined for PECs prepared at pH 3.6, and lowest at pH 4.6, independently of the used acid and PEC concentration. Sample structure estimation was based on apparent viscosities (ηmin at 100 s-1/ηmax at 22.2 s-1). The highest η at concentration of 4% had samples prepared with AA at pH 5.6 (1440/5450 mPa·s), and lowest with HA at pH 4.6 (979/3440 mPa·s). At concentration of 2%, highest η had samples prepared with HA at pH 3.6 (557/2010 mPa·s), and lowest with HA at pH 4.6 (198/692 mPa·s). It can be concluded that acid choice and pH of medium significantly influenced the interaction intensity between polymers, and consequently, solid PECs structure and rheological characteristics after hydration, which can be reflected in active substance release kinetics.", publisher = "Farmaceutska komora Crne Gore, Univerzitet Crne Gore, Medicinski fakultet, studijski program-farmacija", journal = "Treći kongres farmaceuta Crne Gore sa međunarodnim učešćem, 2019. Budva, Bečići, Crna Gora, Zbornik sažetaka", title = "Razvoj nosača lekovitih supstanci tipa polielektrolitnih kompleksa hitozan/ksantan: karakterizacija procesa rehidratacije in vitro, Development of drug delivery systems based on chitosan/xanthan polyelectrolyte complexes: in vitro characterization of rehydration process", pages = "224-225", url = "https://hdl.handle.net/21.15107/rcub_farfar_5368" }
Ćirić, A.,& Đekić, L.. (2019). Razvoj nosača lekovitih supstanci tipa polielektrolitnih kompleksa hitozan/ksantan: karakterizacija procesa rehidratacije in vitro. in Treći kongres farmaceuta Crne Gore sa međunarodnim učešćem, 2019. Budva, Bečići, Crna Gora, Zbornik sažetaka Farmaceutska komora Crne Gore., 224-225. https://hdl.handle.net/21.15107/rcub_farfar_5368
Ćirić A, Đekić L. Razvoj nosača lekovitih supstanci tipa polielektrolitnih kompleksa hitozan/ksantan: karakterizacija procesa rehidratacije in vitro. in Treći kongres farmaceuta Crne Gore sa međunarodnim učešćem, 2019. Budva, Bečići, Crna Gora, Zbornik sažetaka. 2019;:224-225. https://hdl.handle.net/21.15107/rcub_farfar_5368 .
Ćirić, Ana, Đekić, Ljiljana, "Razvoj nosača lekovitih supstanci tipa polielektrolitnih kompleksa hitozan/ksantan: karakterizacija procesa rehidratacije in vitro" in Treći kongres farmaceuta Crne Gore sa međunarodnim učešćem, 2019. Budva, Bečići, Crna Gora, Zbornik sažetaka (2019):224-225, https://hdl.handle.net/21.15107/rcub_farfar_5368 .